In welding test of TCS stainless steel, it was found that impact absorbing energy of heat-affected zone(HAZ)near bond line in welded joint was low.
在TCS不锈钢前期焊接试验中发现其焊接接头热影响区的冲击吸收功值在熔合线附近较低，原因是接头热影响区晶粒粗大所致。
Charpy impact test (V gap): the specified height of pendulum of the one-time blow to V notched specimens in beam state, test specimen is broken by the impact absorbing energy.
夏比（V型缺口）冲击试验：用规定高度的摆锤对处于简支梁状态的V型缺口试样进行一次性打击，测量试样折断时冲击吸收功的试验。
In welding test of TCS stainless steel, it was found that impact absorbing energy of heat-affected zone(HAZ)near bond line in welded joint was low. The reason is coarse grain in HAZ.
在T CS 不锈钢前期焊接试验中发现其焊接接头热影响区的冲击吸收功值在熔合线附近较低，原因是接头热影响区晶粒粗大所致。